ISO 6957:1988 Copper alloys - Ammonia test for stress corrosion resistance

Abbreviation
ISO 6957:1988
Valid from
15/09/1988

Information provider
Standards New Zealand
Author
International Organization for Standardization
Information type
ISO Standard


Description

Specifies a test, using an ammoniacal atmosphere, for the detection of applied or residual stresses which can cause failure of the material in service or storage through stress corrosion cracking. The severity of the method can be regulated by changing the pH value. In an informative annex, recommendations are given for the choice of pH-values.

 

 

For assistance with locating previous versions, please contact the information provider.
View on Information Provider website
For assistance with locating previous versions, please contact the information provider.
This resource is cited by:

ISO 6957:1988 Copper alloys - Ammonia test for stress corrosion resistance

This document is CITED BY:

ISO 6957:1988 Copper alloys - Ammonia test for stress corrosion resistance

Description

Specifies a test, using an ammoniacal atmosphere, for the detection of applied or residual stresses which can cause failure of the material in service or storage through stress corrosion cracking. The severity of the method can be regulated by changing the pH value. In an informative annex, recommendations are given for the choice of pH-values.

 

 

View on Information Provider website
ISO 6957:1988 Copper alloys - Ammonia test for stress corrosion resistance
Description

Specifies a test, using an ammoniacal atmosphere, for the detection of applied or residual stresses which can cause failure of the material in service or storage through stress corrosion cracking. The severity of the method can be regulated by changing the pH value. In an informative annex, recommendations are given for the choice of pH-values.

 

 

View on Information Provider website
This resource does not cite any other resources.

ISO 6957:1988 Copper alloys - Ammonia test for stress corrosion resistance

This resource does not CITE any other resources.
Feedback